316L Prodec Stainless

316/316L Stainless Steel

Generally,  grade 316/316L (UNS S31600 / S31603)  is dual-certified to meet both 316 and 316L. Alloy 316/316L is ideally suited for applications requiring corrosion resistance superior to Type 304 and has good elevated temperature strength.

General Properties

Alloy 316/316L is molybdenum-bearing austenitic stainless steel. The higher nickel and molybdenum content in this grade allows it to demonstrate better overall corrosion resistant properties than 304, especially with regard to pitting and crevice corrosion in chloride environments. In addition, Alloy 316/ 316L provides excellent elevated temperature tensile, creep and stress-rupture strengths, as well as outstanding formability and weldability. 316L is the lower carbon version of 316 and is immune from sensitization; therefore, it is very frequently used in heavy gauge welded components.

Specifications: UNS S31600 / S31603

Applications:

1.Food preparation equipment, especially in chloride environments
2.Chemical processing, equipment
3.Laboratory benches and equipment
4.Rubber, plastics, pulp & paper machinery
5.Pollution control equipment
6.Boat fittings, value and pump trim
7.Heat exchangers
8.Pharmaceutical and textile industries
9.Condensers, evaporators and tanks

Standards:

1.ASTM/ASME: UNS S31600 / S31603
2.EURONORM: X1 CrNiMo 17 12 2 / X3 CrNiMo 17 12 2
3.AFNOR: Z 6 CND 17-11 / Z 2 CND 17-12
4.DIN: 1.4401 / 1.4404

Corrosion Resistance:

1.Generally more resistant than 304 in range of atmospheric environments and many corrosive media due to the increased chromium and molybdenum content.

2.Subject to pitting and crevice corrosion in warm chloride environments, and to stress corrosion cracking above about 122°F (50°C).

3.Considered resistant to potable water with up to about 1000mg/L chlorides at ambient temperatures, reducing to about 500mg/L at 140°F (60°C).

4.Usually regarded as the “marine grade stainless steel” – but is not resistant to warm sea water.

Heat Resistance:

1.Good oxidation resistance in intermittent service to 1600°F (870°C) and in continuous service to 1700°F (925°C)

2.Grade 316L is more resistant to carbide precipitation.

Welding Characteristics:

1.Excellent weldability by all standard fusion methods, both with and without filler metals.

2.Heavy welded sections in Grade 316 require post-weld annealing for maximum corrosion resistance, this is not required for grade 316L.

Heat Treatment:

1.Annealing temperature range is 1900 to 2100°F (1038 to 1149°C).

2.Cannot be hardened by heat treatment.

3.Special consideration is needed to compensate for a higher coefficient of thermal expansion to avoid warping and distortion.

Processing – Hot Forming:

1.Most producers recommend a maximum forging temperature between 2100°F and 2300°F

2.Do not forge below 1700°F (927°C) Best

3.Corrosion resistance is obtained if the forgings are given a final anneal.

Processing – Cold Forming:

1.316/316L types being extremely tough and ductile, can be readily cold worked such as roll form, swaging, cold heading, deep drawing, bent, etc., without difficulty

2.Severely cold formed parts should be annealed to remove stresses.

Machineability:

1.Type 316/316L is somewhat more difficult to machine than Type 304 because of its toughness.
2.316/316L machines with chip characteristics that are tough and strong.
3.Chip breakers and curlers are advised.
4.As large a tool as possible and great amounts of cutting fluid should be used.
5.Heavy positive feeds at low speeds should be considered since 316/316L work hardens rapidly.

Chemical Properties:

 

C

Mn

Si

P

S

Cr

Mo

Ni

N

316
(S31600)

0.08
max

2.0
max

0.75
max

0.045
max

0.03
max

min: 16.0
max: 18.0

min: 2.0
max: 3.0

min: 10.0
max: 14.0

0.10
max

316L
(S31603)

0.03
max

2.0
max

0.75
max

0.045
max

0.03
max

min: 16.0
max: 18.0

min: 2.0
max: 3.0

min: 10.0
max: 14.0

0.10
max

Mechanical Properties:

Grade

Tensile Strength
ksi (min)

Yield Strength
0.2% ksi (min)

Elongation %

Hardness (Brinell) MAX

Hardness
(Rockwell B) MAX

316
(S31600)

75

30

40

217

95

316L
(S31603)

70

25

40

217

95

Physical Properties:

Density
lbm/in3

Thermal Conductivity
(BTU/h ft. °F)

Electrical
Resistivity
(in x 10-6)

Modulus of
Elasticity
(psi x 106

Coefficient of
Thermal Expansion
(in/in)/°F x 10-6

Specific Heat
(BTU/lb/°F)

Melting
Range (°F)

0.29 at 68°F

100.8 at 68 212°F

29.1 at 68°F

29

8.9 at 32 – 212°F

0.108 at 68°F

2500 to 2550

 

 

 

 

9.7 at 32 – 1000°F

0.116 at 200°F

 

 

 

 

 

11.1 at 32 – 1500°F