410 Steel Stainless

Meatotino Aoao

Uʻamea filogia 410 o le faavae, faamoemoega aoao o uamea stainless martensitic ua faaaogāina mo vaega faamamafa maualuga ma maua ai tetee lelei corrosion faaopoopo i le malosi sili ma le maaa. Uʻamea filogia 410 o loo i ai a itiiti mai o le 11.5% chromium mea ua tonu lava lava e faaalia ai meatotino tetee corrosion i atmospheres vaivai, ausa, ma le tele o siosiomaga agamalu vailaau. O se vasega faamoemoega aoao o le e masani ona tuuina atu i le Faamaaaina ae tulaga machineable pea mo talosaga ai le malosi sili ma le vevela feololo ma corrosion tetee e manaomia. Uʻamea filogia 410 faaaliga tetee corrosion maualuga pe o loo ua maaa, agamalu, ma polesi.

Auiliili: UNS S41000

talosaga:

Talosaga e manaomia tetee feololo corrosion ma meatotino masini maualuga e lelei mo uʻamea filogia 410. Faataitaiga o talosaga e faaaoga soo uʻamea filogia 410 e aofia ai:

1.Cutlery
2.Steam ma kasa tupine blades
3.Kitchen ipu
4.Bolts, fatu, fao
5.Pump ma alatoto vaega ma ufanafana
6.Mine apefai solovae
7.Dental ma taotoga meafaigaluega
8.Nozzles
uamea 9.Hardened polo ma nofoa mo pamu lelei suauu

Tulaga Faatonuina:

1.ASTM / ASME: UNS S41000
2.EURONORM: FeMi35Cr20Cu4Mo2
3.DIN: 2,4660
4.Good corrosion tetee atu i corrosion ea, vai potable, ma le agamalu aati siosiomaga
5.Its aafia i gaoioiga i aso uma (o taaloga, sauniuniga meaai) e masani faamalieina pe a faataunuuina le faamamaina e tatau ai ina ua uma ona aafia i faaaogaina
tetee corrosion 6.Good e concentrations maualalo o acids faatulagaina ma minerale agamalu

Tetee Corrosion:

Uiga maopoopo

1.Readily ueloina e auala tulaga uma
faaitiitia 2.To le tulaga lamatia o le faapapaina o, ua fautuaina e le faia muamua o le vevela o le galuega fasi e 350 i le 400 o F (177 i le 204 o C)
3.Post weld annealing Ua fautuaina e taofi aupito maualuga ductility
4.The ituaiga galuega vevela lelei o le 2000 i le 2200 o F (1093 i le 1204 o C)
5.Do le galulue i mea nei o loo i lalo 1650 o F (899 o C)

Togafitiga vevela

Meatotino vailaau:

 

C

Mn

Si

P

S

CR

Ni

410

0,15 Max

1.00 Max

1.00 Max

0,04 Max

0,03 Max

minu: 11.5
Max: 13.5

0.50 Max

Meatotino masini:

vasega

Tensile ksi Malosi (faasao) min

Gauai Malosi 0.2% ksi aveesea (faasao) min

Elongation (% i le 50mm) min

Maaa (Brinell) Max

Maaa (Rockwell B) Max

410

65 (450)

30 (205)

20

217

96

Meatotino masini o le vevela Faia 410:

Togafitiga vevela

T410 (0.14% C) faamaaa 1800 ° F (982 ° C)

Rockwell maaa

0.2% YS, Ksi (faasao)

UTS, Ksi (faasao)

Annealed *

81 HRB

45,4 (313)

80,4 (554)

 Faamaaaina & agamalu 400 ° F (204 ° C)

43 HRC

156,1 (1076)

 202,9 (1399)

 Faamaaaina & agamalu 550 ° F (288 ° C)

 40 HRC

148,3 (1022)

 187,0 (1289)

Faamaaaina & agamalu 600 ° F (316 ° C)

40 HRC

148,8 (1026)

186,1 (1283)

Faamaaaina & agamalu 800 ° F (427 ° C)

41 HRC

132,9 (916)

188,5 (1300)

Faamaaaina & agamalu 900 ° F (482 ° C)

41 HRC

122,6 (845)

154,3 (1063)

Faamaaaina & agamalu 1000 ° F (538 ° C)

35 HRC

127,9 (882)

154,3 (1063)

Faamaaaina & agamalu 1200 ° F (649 ° C)

98 HRB

85,5 (589)

111,2 (767)

Meatotino faaletino:

Density
lbm/in3

Conductivity vevela
(BTU/h ft. °F)

Eletise
Resistivity
(in x 10-6 )

Modulus o
Elasticity
(psi x 106

Coefficient o
Thermal Expansion
(in/in)/
°F x 10-6

Faapitoa le vevela
(BTU/lb/
°F)

Le teʻa
Range
(°F)

i le 68 ° F: 0,276

14.4 i le 212 ° F

56 i le 68 ° F

29

5,90 i le 68 - 392 ° F

0,11 i le 68 ° F e 212 ° F

2700 i le 2790

 

 

 

 

6.5 i le 68 - 1112 ° F