410 igwe anaghị agba nchara

General Properties

Alloy 410 bụ isi, n'ozuzu nzube martensitic igwe anaghị agba nchara na-eji maka ukwuu mesiri akụkụ ma na-enye ezi corrosion eguzogide plus elu ike na ekweghị ekwe. Alloy 410 nwere a kacha nta nke 11.5% chromium nke dị zuru ezu iji gosi na corrosion eguzogide Njirimara na nwayọọ atmospheres, uzuoku, na ọtụtụ nwayọọ chemical gburugburu. Ọ bụ a n'ozuzu nzube ọkwa na a na-ọnọ na obi tara mmiri ma ka machineable ọnọdụ maka ngwa ebe elu ike na agafeghị oke okpomọkụ na corrosion na-eguzogide na-achọrọ. Alloy 410 ngosipụta kacha corrosion eguzogide mgbe ọ e obi tara mmiri, na-ebelata, na mgbe ahụ-egbu maramara.

Nkọwa: uns S41000

ngwa:

Ngwa ka a na-agafeghị oke corrosion na-eguzogide na elu na n'ibu Njirimara dị mma maka Alloy 410. Ihe Nlereanya nke ngwa na-ugboro ugboro ji Alloy 410 na-agụnye:

1.Cutlery
2.Steam na gas tobaim pupụtara
3.Kitchen arịa
4.Bolts, mkpụrụ, kposara
5.Pump na valvụ akụkụ na akụ
6.Mine n'ọkwá rugs
7.Dental na ịwa ahụ ngwá
8.Nozzles
9.Hardened ígwè bọọlụ na oche mmanụ ọma nfuli

Standards:

1.ASTM / ASME: uns S41000
2.EURONORM: FeMi35Cr20Cu4Mo2
3.DIN: 2,4660
4.Good corrosion iguzogide ikuku corrosion, potable mmiri, na mildly corrosive gburugburu
5.Its n'ebe-eme kwa ụbọchị (egwuregwu, nri nkwadebe) bụ n'ozuzu eju afọ mgbe kwesịrị ekwesị ihicha na rụrụ mgbe ikpughe iji
6.Good corrosion iguzogide ala kasịnụ nke dịkwa nwayọọ organic na ịnweta asịd

Corrosion Nguzogide:

ịgbado ọkụ Njirimara

1.Readily welded site nile ọkọlọtọ ụzọ
2.To belata ihe ize ndụ nke cracking, na-atụ aro-eji ikpo ọrụ ibe 350 400 o F (177 na 204 o C)
3.Post Weld annealing na-atụ aro ka na-ejigide kacha ductility
4.The kwesịrị ekwesị na-ekpo ọkụ na-arụ ọrụ nso 2000 2200 o F (1093 ka 1204 o C)
5.Do na-arụ ọrụ a ihe onwunwe n'okpuru 1650 o F (899 o C)

okpomọkụ Ọgwụgwọ

Chemical Properties:

 

C

igwe

si

P

S

ČR

ni

410

0,15 max

1.00 max

1.00 max

0,04 max

0.03 max

min: 11.5
max: 13.5

0,50 max

Mechanical Properties:

mezuwo

Ike ọdụdọ ksi (MPa) min

Ekwenyere Ike 0,2% dechapụ ksi (MPa) min

Elongation (% na 50mm) min

Ekweghị ekwe (Brinell) Max

Ekweghị ekwe (Rockwell B) Max

410

65 (450)

30 (205)

20

217

96

Mechanical Properties nke Okpomọkụ Mesoo 410:

okpomọkụ Ọgwụgwọ

T410 (0.14% C) tara mmiri 1800 ° F (982 ° C)

Rockwell ekweghị ekwe

0.2% YS, Ksi (MPa)

UTS, Ksi (MPa)

Annealed *

81 HRB

45,4 (313)

80,4 (554)

 Obi tara mmiri & n'obi 400 ° F (204 ° C)

43 HRC

156,1 (1076)

 202,9 (1399)

 Obi tara mmiri & n'obi 550 ° F (288 ° C)

 40 HRC

148,3 (1022)

 187,0 (1289)

Obi tara mmiri & n'obi 600 ° F (316 ° C)

40 HRC

148,8 (1026)

186,1 (1283)

Obi tara mmiri & n'obi 800 ° F (427 ° C)

41 HRC

132,9 (916)

188,5 (1300)

Obi tara mmiri & n'obi 900 ° F (482 ° C)

41 HRC

122,6 (845)

154,3 (1063)

Obi tara mmiri & n'obi 1000 ° F (538 ° C)

35 HRC

127,9 (882)

154,3 (1063)

Obi tara mmiri & n'obi 1200 ° F (649 ° C)

98 HRB

85,5 (589)

111,2 (767)

Physical Properties:

Njupụta
lbm/in3

Kwes conductivity
(BTU/h ft. °F)

Ọdụdọ
Resistivity
(in x 10-6 )

Modulus nke
Elasticity
(psi x 106

Ọnụọgụ nke
Thermal Expansion
(in/in)/
°F x 10-6

Specific Okpomọkụ
(BTU/lb/
°F)

-Agbaze
Range
(°F)

na 68 ° F: 0,276

14.4 na 212 ° F

56 na 68 ° F

29

5,90 na 68 - 392 ° F

0,11 na 68 ° F na 212 ° F

2700 ka 2790

 

 

 

 

6.5 na 68 - 1112 ° F